High-resistance electrical heating alloys: |
|
High-resistance electrical heating alloys, such as drawing (or rolling) NiCr (NiCrFe, FeCrAl) wires (strips, bars, or wire coils), are used as made into electrical heating elements and general resistance elements.
|
¤ Chemical constitutions:
|
Alloy material
|
Chemical composition %
|
C
|
P
|
S
|
Mn
|
Si
|
Cr
|
Ni
|
Al
|
Fe
|
others
|
Not more than(≤)
|
Cr20Ni80
|
0.08
|
0.020
|
0.015
|
0.60
|
0.75~1.60
|
20.0~23.0
|
Residual
|
≤0.50
|
≤1.0
|
—
|
Cr30Ni70
|
0.08
|
0.020
|
0.015
|
0.60
|
0.75~1.60
|
28.0~31.0
|
Residual
|
≤0.50
|
≤1.0
|
—
|
Cr15Ni60
|
0.08
|
0.020
|
0.015
|
0.60
|
0.75~1.60
|
15.0~18.0
|
55.0~61.0
|
≤0.50
|
Residual
|
—
|
Cr20Ni35
|
0.08
|
0.020
|
0.015
|
1.00
|
1.00~3.00
|
18.0~21.0
|
34.0~37.0
|
—
|
Residual
|
—
|
Cr20Ni30
|
0.08
|
0.020
|
0.015
|
1.00
|
1.00~2.00
|
18.0~21.0
|
30.0~34.0
|
—
|
Residual
|
—
|
1Cr13Al4
|
0.12
|
0.025
|
0.025
|
0.70
|
≤1.00
|
12.0~15.0
|
—
|
4.0~6.0
|
Residual
|
—
|
0Cr25Al5
|
0.06
|
0.025
|
0.025
|
0.70
|
≤0.60
|
23.0~26.0
|
≤0.60
|
4.5~6.5
|
Residual
|
—
|
0Cr23Al5
|
0.06
|
0.025
|
0.025
|
0.70
|
≤0.60
|
20.5~23.5
|
≤0.60
|
4.2~5.3
|
Residual
|
—
|
0Cr21Al6
|
0.06
|
0.025
|
0.025
|
0.70
|
≤1.00
|
19.0~22.0
|
≤0.60
|
5.0~7.0
|
Residual
|
—
|
1Cr20Al3
|
0.06
|
0.025
|
0.025
|
0.70
|
≤1.00
|
18.0~21.0
|
≤0.60
|
3.0~4.2
|
Residual
|
—
|
0Cr21Al6Nb
|
0.05
|
0.025
|
0.025
|
0.70
|
≤0.60
|
21.0~23.0
|
≤0.60
|
5.0~7.0
|
Residual
|
Nb additions0.5
|
0Cr27Al7Mo2
|
0.05
|
0.025
|
0.025
|
0.20
|
≤0.40
|
26.5~27.8
|
≤0.60
|
6.0~7.0
|
Residual
|
|
|
¤ Resistivity of soft wires: |
Alloy material
|
Diameter(mm)
|
Resistivity(μΩm)(20℃)
|
Cr20Ni80
|
<0.50 0.50~3.00 >3.00
|
1.09±0.05 1.13±0.05 1.14±0.05
|
Cr30Ni70
|
<0.50 ≥0.50
|
1.18±0.05 1.20±0.05
|
Cr15Ni60
|
<0.50 ≥0.50
|
1.12±0.05 1.15±0.05
|
Cr20Ni35
|
Cr20Ni30 <0.50 ≥0.50
|
1.04±0.05 1.06±0.05
|
1Cr13Al4 0Cr25Al5 0Cr23Al5 0Cr21Al6 1Cr20Al3 0Cr21Al6Nb
|
0.03~8.00
|
1.25±0.08 1.42±0.07 1.35±0.06 1.42±0.07 1.23±0.06 1.45±0.07
|
0Cr27Al7Mo2
|
0.03~8.00
|
1.53±0.07
|
|
¤ Specification: mm |
Wires
|
Paint-coated(uncoated) wires
|
Uncoated wires
|
Diameter
|
0.02~1.2
|
Diameter
|
>0.02~6.0
|
Sheet, strip
|
Thickness
|
0.05~3.5
|
Width
|
6~100
|
Flat wires
|
Thickness
|
0.08~0.8
|
Width
|
0.2~10.0
|
|
¤ Resistivity of strip materials: |
Alloy material
|
Diameter(mm)
|
Resistivity(μΩm)20℃
|
Cr20Ni80
|
≤0.80 >0.80~3.00 >3.00
|
1.09±0.05 1.13±0.05 1.14±0.05
|
Cr30Ni70
|
≤0.80 >0.80~3.00 >3.00
|
1.18±0.05 1.19±0.05 1.20±0.05
|
Cr15Ni60
|
≤0.80 >0.80~3.00 >3.00
|
1.11±0.05 1.14±0.05 1.15±0.05
|
Cr20Ni35 Cr20Ni30
|
<0.80 ≥0.80
|
1.04±0.05 1.06±0.05
|
1Cr13Al4 0Cr25Al5 0Cr23Al5 0Cr21Al6 1Cr20Al3 0Cr21Al6Nb 0Cr27Al7Mo2
|
0.05~3.50
|
1.25±0.08 1.42±0.07 1.35±0.07 1.42±0.07 1.23±0.07 1.45±0.07 1.53±0.07
|
|